Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Ultramid® B3EG4 SI UN - PA6-GF20 - BASF

Check here, which other Ultramid B datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - Mechanical properties - Thermal properties - Other properties - Material specific properties - Diagrams

Any use of this information falls under the rules of our disclaimer.

Product Texts

Glass fibre-reinforced injection moulding grade, with excellent surface quality especially suitable for the production of visible parts. Optimum surface quality is generally obtained at a very high injection speed.

Processing/Physical Characteristics	dry / cond	Unit	Test Standard
ISO Data
Melt volume-flow rate, MVR	25 / *	cm³/10min	ISO 1133
Temperature	275 / *	°C	-
Load	5 / *	kg	-
Molding shrinkage, parallel	0.4 / *	%	ISO 294-4, 2577
Molding shrinkage, normal	0.7 / *	%	ISO 294-4, 2577

Mechanical properties	dry / cond	Unit	Test Standard
ISO Data
Tensile Modulus	7150 / 3750	MPa	ISO 527
Stress at break	150 / 80	MPa	ISO 527
Strain at break	3.8 / 14	%	ISO 527
Charpy impact strength, +23°C	65 / 100	kJ/m²	ISO 179/1eU
Charpy impact strength, -30°C	55 / 55	kJ/m²	ISO 179/1eU
Charpy notched impact strength, +23°C	9 / 19	kJ/m²	ISO 179/1eA
Charpy notched impact strength, -30°C	7.5 / 7.5	kJ/m²	ISO 179/1eA

Thermal properties	dry / cond	Unit	Test Standard
ISO Data
Melting temperature, 10°C/min	220 / *	°C	ISO 11357-1/-3
Temp. of deflection under load, 1.80 MPa	200 / *	°C	ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa	215 / *	°C	ISO 75-1/-2

Other properties	dry / cond	Unit	Test Standard
Density	1270 / *	kg/m³	ISO 1183

Material specific properties	dry / cond	Unit	Test Standard
ISO Data
Viscosity number	148 / *	cm³/g	ISO 307, 1157, 1628

Diagrams

Characteristics

Processing

Injection Molding

Delivery form

Pellets, Natural Color

Additives

Release agent

Regional Availability

North America, Europe

Other text information

Injection molding

PREPROCESSING
Pre/Post-processing, max. allowed water content: .05 %
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 4 - 8 h

PROCESSING
injection molding, Melt temperature, range: 260 - 280 °C
injection molding, Melt temperature, recommended: 270 °C
injection molding, Mold temperature, range: 80 - 110 °C
injection molding, Mold temperature, recommended: 100 °C
injection molding, Dwell time, thermoplastics: 10 min

Chemical Media Resistance

Acids
	Acetic Acid (5% by mass) (23°C)
	Citric Acid solution (10% by mass) (23°C)
	Lactic Acid (10% by mass) (23°C)
	Hydrochloric Acid (36% by mass) (23°C)
	Nitric Acid (40% by mass) (23°C)
	Sulfuric Acid (38% by mass) (23°C)
	Sulfuric Acid (5% by mass) (23°C)
	Chromic Acid solution (40% by mass) (23°C)
Bases
	Sodium Hydroxide solution (35% by mass) (23°C)
	Sodium Hydroxide solution (1% by mass) (23°C)
Alcohols
	Isopropyl alcohol (23°C)
	Methanol (23°C)
	Ethanol (23°C)
Hydrocarbons
	n-Hexane (23°C)
	Toluene (23°C)
	iso-Octane (23°C)
Ketones
	Acetone (23°C)
Ethers
	Diethyl ether (23°C)
Salt solutions
	Sodium Chloride solution (10% by mass) (23°C)
	Sodium Hypochlorite solution (10% by mass) (23°C)
	Zinc Chloride solution (50% by mass) (23°C)
Other
	Ethyl Acetate (23°C)
	Hydrogen peroxide (23°C)
	Ethylene Glycol (50% by mass) in water (108°C)
	Water (23°C)

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com